| 类型 | 标准料 |
| 牌号 | C9021 |
| 销售方式 | 品牌经销 |
| 用途级别 | 板材级,照明灯具,运动器材,医用级,汽车部件,电子电器部件,薄膜级 |
| 品牌 | POM |
| 厂家(产地) | 德国赫斯特 |
| 加工级别 | 注塑级 |
| 特性级别 | 标准级,阻燃级,耐水解,耐磨,高流动 |
聚甲醛（POM）共聚物 Celanese Corporation 产品说明：
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 03-002
POM copolymer
Standard-Injection molding type with high rigidity, hardness and
toughness; good chemical resistance to solvents, fuel and strong
alkalis as well as good hydrolysis resistance; high resistance to
thermal and oxidative degradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470
UL-registration for all colours and a thickness more than 1.5 mm as
UL 94 HB, temperature index UL 746 B electrical 110°C, mechanical
90°C.
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more
than 1 mm.
Ranges of applications: automotive engineering, precision
engineering, electric and electronical industry, domestic
appliances.
FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
Hostaform® C 9021 物性表
| 基本信息 | |
| |
| 特性 | 刚性，高 抗溶剂性 耐化学性良好 耐碱 耐燃油性 耐水解性 韧性良好 硬度高 |
| 用途 | 电气/电子应用领域 电器用具 工程配件 汽车领域的应用 |
| 机构评级 | FDA 21 CFR 177.2470 欧洲 10/1/2011 12:00:00 AM |
| RoHS 合规性 | 联系制造商 |
| 加工方法 | 注射成型 |
| 多点数据 | Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) |
| 树脂ID (ISO 1043) | POM |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.41 | g/cm3 | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 8.00 | cm3/10min | ISO 1133 |
| 收缩率 | | | ISO 294-4 |
| 垂直流动方向 | 1.8 | % | ISO 294-4 |
| 流动方向 | 2.0 | % | ISO 294-4 |
| 吸水率 (饱和, 23°C) | 0.65 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | 2850 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 64.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 9.0 | % | ISO 527-2/1A/50 |
| 标称拉伸断裂应变 | 30 | % | ISO 527-2/1A/50 |
| 拉伸蠕变模量 | | | ISO 899-1 |
| 1 hr | 2500 | MPa | ISO 899-1 |
| 1000 hr | 1300 | MPa | ISO 899-1 |
| 弯曲模量 (23°C) | 2700 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | | | ISO 179/1eA |
| -30°C | 6.0 | kJ/m2 | ISO 179/1eA |
| 23°C | 6.5 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 | | | ISO 179/1eU |
| -30°C | 160 | kJ/m2 | ISO 179/1eU |
| 23°C, 局部断裂 | 180 | kJ/m2 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 热变形温度 (1.8 MPa, 未退火) | 104 | °C | ISO 75-2/A |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 | | | ISO 11359-2 |
| 流动 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度 | 35 | kV/mm | IEC 60243-1 |
| 相对电容率 | | | IEC 60250 |
| 100 Hz | 4.00 | | IEC 60250 |
| 1 MHz | 4.00 | | IEC 60250 |
| 耗散因数 | | | IEC 60250 |
| 100 Hz | 2.0E-3 | | IEC 60250 |
| 1 MHz | 5.0E-3 | | IEC 60250 |
| 漏电起痕指数 | 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | | | UL 94 |
| 1.50 mm | HB | | UL 94 |
| 3.00 mm | HB | | UL 94 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| Density of Melt | 1.200 | g/cm3 | 内部方法 |
| Ejection Temperature | 165 | °C | 内部方法 |
| Specific Heat Capacity of Melt | 2210 | J/kg/°C | 内部方法 |
| Thermal Conductivity of Melt | 0.16 | W/m/K | 内部方法 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| Effective Thermal Diffusivity | 0.0485 | cSt | 内部方法 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 120 到 140 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 料斗温度 | 20.0 到 30.0 | °C | |
| 料筒后部温度 | 170 到 180 | °C | |
| 料筒中部温度 | 180 到 190 | °C | |
| 料筒前部温度 | 190 到 200 | °C | |
| 射嘴温度 | 190 到 210 | °C | |
| 加工（熔体）温度 | 190 到 210 | °C | |
| 模具温度 | 80.0 到 120 | °C | |
| 注塑压力 | 60.0 到 120 | MPa | |
| 注射速度 | 慢到中等 | | |
| 保压 | 60.0 到 120 | MPa | |
| 背压 | 0.00 到 4.00 | MPa | |
生成海报